Lezi zakhiwo zicaciswe emikhiqizweni egoqeke isicaba (ipuleti, ishidi, nekhoyili) ku-ASTM A240/A240M.Izakhiwo ezifanayo kodwa ezingafani ngempela zicaciswe kweminye imikhiqizo efana nepayipi nebha ngokucaciswa kwazo.

Ukwakheka

Ithebula 1.Ububanzi bokwakhiwa kwensimbi engagqwali engu-316L.

Ibanga		C	Mn	Si	P	S	Cr	Mo	Ni	N
316L	Okuncane	-	-	-	-	-	16.0	2.00	10.0	-
316L	Ubukhulu	0.03	2.0	0.75	0.045	0.03	18.0	3.00	14.0	0.10

Izakhiwo Zemishini

316L/S31603 insimbi engagqwali 7.0*0.3 mm yesishintshi sokushisa

Ithebula 2.Izakhiwo zemishini ye-316L yensimbi engagqwali.

Ibanga	I-Tensile Str (MPa) imiz	Yield Str 0.2% Ubufakazi (MPa) min	Elong (% ku-50 mm) min	Ukuqina
Ibanga	I-Tensile Str (MPa) imiz	Yield Str 0.2% Ubufakazi (MPa) min	Elong (% ku-50 mm) min	I-Rockwell B (HR B) ubuningi	I-Brinell (HB) ubuningi
316L	485	170	40	95	217

Izakhiwo Zomzimba

316L/S31603 insimbi engagqwali 7.0*0.3 mm yesishintshi sokushisa

Ithebula 3.Izakhiwo ezibonakalayo ezijwayelekile zezinsimbi ezingenasici ze-316-grade.

Ibanga	Ukuminyana (kg/m3)	I-Elastic Modulus (GPA)	I-Co-eff esho ukunwetshwa kwe-Thermal (µm/m/°C)			I-Thermal Conductivity (W/mK)		Ukushisa Okuthize 0-100 °C (J/kg.K)	I-Elec Resistivity (nΩ.m)
Ibanga	Ukuminyana (kg/m3)	I-Elastic Modulus (GPA)	0-100 °C	0-315 °C	0-538 °C	Ku-100 °C	Ku-500 °C	Ukushisa Okuthize 0-100 °C (J/kg.K)	I-Elec Resistivity (nΩ.m)
316/L/H	8000	193	15.9	16.2	17.5	16.3	21.5	500	740

Ukuqhathaniswa Kwencazelo Yebanga

316L/S31603 insimbi engagqwali 7.0*0.3 mm yesishintshi sokushisa

Ithebula 4.Imininingwane yebanga ye-316L yensimbi engagqwali.

Ibanga	Inombolo ye-UNS	Old British		I-Euronorm		I-Swedish SS	I-JIS yaseJapane
Ibanga	Inombolo ye-UNS	BS	En	No	Igama	I-Swedish SS	I-JIS yaseJapane
316L	I-S31603	316S11	-	1.4404	I-X2CrNiMo17-12-2	2348	I-SUS 316L

Thumela i-imeyili kithi

Imininingwane Yomkhiqizo

Omaka bomkhiqizo

Ukwakheka

316L/S31603 insimbi engagqwali 7.0*0.3 mm yesishintshi sokushisa

Ithebula 1.Ububanzi bokwakhiwa kwensimbi engagqwali engu-316L.

Ibanga		C	Mn	Si	P	S	Cr	Mo	Ni	N
316L	Okuncane	-	-	-	-	-	16.0	2.00	10.0	-
316L	Ubukhulu	0.03	2.0	0.75	0.045	0.03	18.0	3.00	14.0	0.10

Izakhiwo Zemishini

316L/S31603 insimbi engagqwali 7.0*0.3 mm yesishintshi sokushisa

Ithebula 2.Izakhiwo zemishini ye-316L yensimbi engagqwali.

Ibanga	I-Tensile Str (MPa) imiz	Yield Str 0.2% Ubufakazi (MPa) min	Elong (% ku-50 mm) min	Ukuqina
Ibanga	I-Tensile Str (MPa) imiz	Yield Str 0.2% Ubufakazi (MPa) min	Elong (% ku-50 mm) min	I-Rockwell B (HR B) ubuningi	I-Brinell (HB) ubuningi
316L	485	170	40	95	217

Izakhiwo Zomzimba

316L/S31603 insimbi engagqwali 7.0*0.3 mm yesishintshi sokushisa

Ithebula 3.Izakhiwo ezibonakalayo ezijwayelekile zezinsimbi ezingenasici ze-316-grade.

Ibanga	Ukuminyana (kg/m3)	I-Elastic Modulus (GPA)	I-Co-eff esho ukunwetshwa kwe-Thermal (µm/m/°C)			I-Thermal Conductivity (W/mK)		Ukushisa Okuthize 0-100 °C (J/kg.K)	I-Elec Resistivity (nΩ.m)
Ibanga	Ukuminyana (kg/m3)	I-Elastic Modulus (GPA)	0-100 °C	0-315 °C	0-538 °C	Ku-100 °C	Ku-500 °C	Ukushisa Okuthize 0-100 °C (J/kg.K)	I-Elec Resistivity (nΩ.m)
316/L/H	8000	193	15.9	16.2	17.5	16.3	21.5	500	740