Izicelo ze-Grade 310/310S Stainless Steel
310 310S amashubhu ahlanganisiwe/amashubhu e-capillary
Izicelo Ezijwayelekile zeBanga 310/310S zisetshenziswa kumshini wokubala umbhede one-fluidised, okokhela, amashubhu akhazimulayo, iziphanyeko zamashubhu zokucwenga uphethiloli kanye namabhoyela esitimu, izingxenye zangaphakathi zegesi yamalahle, amabhodwe omthofu, ama-thermowells, amabhawodi ehange aphikisayo, izibasi namakamelo avuthayo, ama-muffles, amakhava e-annealing, ama-saggers, imishini yokucubungula ukudla, izakhiwo ze-cryogenic.
Izakhiwo ze-Grade 310/310S Stainless Steel
310 310S amashubhu ahlanganisiwe/amashubhu e-capillary
Lawa mabanga aqukethe u-25% we-chromium no-20% we-nickel, okuwenza amelane kakhulu ne-oxidation nokugqwala.I-Grade 310S inguqulo yekhabhoni ephansi, ethambekele kancane ekugxilweni nasekuqwashiseni enkonzweni.I-chromium ephezulu kanye nokuqukethwe kwe-nickel emaphakathi kwenza lezi zinsimbi zikwazi ukusetshenziswa ekunciphiseni i-sulphur atmospheres equkethe i-H2S.Asetshenziswa kakhulu ezindaweni eziphansi ze-carburising, njengoba kutholakala ezindaweni ze-petrochemical.Ukuze uthole izimo ezinzima kakhulu ze-carburising, ezinye izingxube ezimelana nokushisa kufanele zikhethwe.Ibanga 310 alituswa ukuthi licime uketshezi njalo njengoba lihlushwa ukushaqeka okushisayo.Ibanga livame ukusetshenziselwa izinhlelo zokusebenza ze-cryogenic, ngenxa yokuqina kwayo kanye nokufinyeleleka okuphansi kazibuthe.
310 310S amashubhu ahlanganisiwe/amashubhu e-capillary
Ngokufana nezinye izinsimbi ezingenasici ze-austenitic, lawa mabanga awakwazi ukwenziwa lukhuni ukwelashwa okushisa.Zingenziwa lukhuni ngomsebenzi obandayo, kodwa lokhu akuvamile ukwenziwa.
Ukwakhiwa Kwekhemikhali Yebanga 310/310S Insimbi Engagqwali
Ukwakheka kwamakhemikhali ebangeni lama-310 kanye nebanga lama-310S ensimbi engagqwali kufingqiwe kuthebula elilandelayo.
310 310S amashubhu ahlanganisiwe/amashubhu e-capillary
Ithebula 1.Ukwakheka kwamakhemikhali % webanga 310 kanye nensimbi engagqwali engu-310S
| Ukwakheka Kwamakhemikhali | 310 | 310S |
| Ikhabhoni | 0.25 ubuningi | 0.08 ubuningi |
| IManganese | 2.00 ubuningi | 2.00 ubuningi |
| I-silicon | 1.50 ubuningi | 1.50 ubuningi |
| Phosphorus | 0.045 ubuningi | 0.045 ubuningi |
| Isibabule | 0.030 ubuningi | 0.030 ubuningi |
| I-Chromium | 24.00 - 26.00 | 24.00 - 26.00 |
| I-Nickel | 19.00 - 22.00 | 19.00 - 22.00 |
Izakhiwo Zemishini Yebanga 310/310S Insimbi Engagqwali
Izakhiwo zemishini zebanga lama-310 kanye nebanga lama-310S zensimbi engagqwali zifingqiwe kuthebula elilandelayo.
Ithebula 2.Izakhiwo zemishini zebanga 310/310S zensimbi engagqwali
| Izakhiwo Zemishini | 310/ 310S |
| Ibanga 0.2 % I-Proof Stress MPa (min) | 205 |
| I-Tensile Strength MPa (min) | 520 |
| Ubude % (imizuzu) | 40 |
| Ukuqina (HV) (ubukhulu) | 225 |
Izici Zomzimba Zensimbi Engagqwali yeFerritic
Izakhiwo ezibonakalayo zebanga lama-310 kanye nebanga lama-310S zensimbi engagqwali zifingqiwe kuthebula elilandelayo.
Ithebula 3.Izakhiwo ezibonakalayo zebanga 310/310S insimbi engagqwali
| Izakhiwo | at | Inani | Iyunithi |
| Ukuminyana |
| 8,000 | Kg/m3 |
| I-Electric Conductivity | 25°C | 1.25 | %IACS |
| Ukungazweli Kagesi | 25°C | 0.78 | I-Micro ohm.m |
| I-Modulus ye-Elasticity | 20°C | 200 | I-GPa |
| Shear Modulus | 20°C | 77 | I-GPa |
| Isilinganiso sikaPoisson | 20°C | 0.30 |
|
| Ukuncibilika kweRnage |
| 1400-1450 | °C |
| Ukushisa Okuthize |
| 500 | J/kg.°C |
| I-Relative Magnetic Permeability |
| 1.02 |
|
| I-Thermal Conductivity | 100°C | 14.2 | W/m.°C |
| I-Coefficient of Expansion | 0-100°C | 15.9 | /°C |
| 0-315°C | 16.2 | /°C | |
| 0-540°C | 17.0 | /°C |