Ukwakheka Kwamakhemikhali
Ingxubevange C2000 ukwakheka kwamakhemikhali
Ukwakheka kwamakhemikhali e-Hastelloy C-2000 kukhonjisiwe etafuleni elingezansi:
| Isici | Ubuncane % | Ubuningi % |
|---|---|---|
| Cr | 22.00 | 24.00 |
| Mo | 15.00 | 17.00 |
| Fe | - | 3.00 |
| C | - | 0.01 |
| Si | - | 0.08 |
| Co | - | 2.00 |
| Mn | - | 0.50 |
| P | - | 0.025 |
| S | - | 0.01 |
| Cu | 1.30 | 1.90 |
| Al | - | 0.50 |
| Ni | bal |
Ingxubevange Imininingwane
Ukuminyana kwe-Hastelloy C-2000, indawo encibilikayo, i-coefficient yokunwetshwa, kanye nemodulus yokunwebeka kukhonjisiwe kuthebula elingezansi:
| Ukuminyana | I-Melting Point | I-Coefficient of Expansion | I-Modulus of Rigidity | I-Modulus ye-Elasticity |
|---|---|---|---|---|
| 8.5 g/cm³ | 1399 °C | 12.4 μm/m °C (20 – 100 °C) | 79 kN/mm² | 206 kN/mm² |
| 0.307 lb/in³ | 2550 °F | 6.9 x 10-6ku-°F (70 – 212 °F) | 11458 k | 29878 nxa |
Ukwelashwa kokushisa kwezingxenye eziqediwe
Ingxubevange C2000 ukwakheka kwamakhemikhali
Ukwelashwa okujwayelekile kokushisa kwe-Hastelloy C-2000:
| Umbandela njengoba uhlinzekwe yi-AWI | Uhlobo | Izinga lokushisa | Isikhathi | Ukupholisa |
|---|---|---|---|---|
| I-Annealed noma i-Spring Temper | Yehlisa Ingcindezi | 400 – 450 °C (750 – 840 °F) | 2 Hr | Umoya |
Izakhiwo
Izakhiwo ezijwayelekile zemishini ye-Hastelloy C-2000:
| I-Annealed | ||
|---|---|---|
| Cishe.amandla aqinile | <1000 N/mm² | <145 ksi |
| Cishe.izinga lokushisa lokusebenza kuye ngomthwalo ** kanye nendawo | -200 kuya +400 °C | -330 kuya +750 °F |
| I-Spring Temper | ||
|---|---|---|
| Cishe.amandla aqinile | 1300 - 1600 N/mm² | 189 – 232 ksi |
| Cishe.izinga lokushisa lokusebenza kuye ngomthwalo ** kanye nendawo | -200 kuya +400 °C | -330 kuya +750 °F |